Abstract
The nanocomposite of hard (BaFe12O19)/soft ferrite (Ni0.8Zn0.2 Fe2O4) was prepared by the sol–gel process, and then the polyaniline(PANI)/polypyrrole(PPY)-BaFe12O19/Ni0.8Zn0.2Fe2O4 was produced by in situ polymerization method. The structures, morphology and electromagnetic properties of the samples were characterized by various instruments. XRD, TEM, and FTIR analysis indicated that BaFe12O19/Ni0.8Zn0.2Fe2O4 ferrite were homogenously enwrapped by PANI(PPY) coating. The VSM and SDY-4 measurement show that the magnetic properties of the composites decreased with the increase in PANI(PPY) amount, However, the electrical conductivity is on the contrary. The electromagnetic properties of the composites were much better than BaFe12O19/Ni0.8Zn0.2Fe2O4 in the frequency range of 2–15GHz, which mainly depends on the dielectric loss of PANI(PPY). A minimum reflection loss of the PANI(PPY)-BaFe12O19/Ni0.8Zn0.2Fe2O4 ferrite nanocomposite is −19.7dB(−21.5dB) at the frequency of 7.3GHz (10.7GHz).
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.