Abstract
Abstract Various volume fractions of perovskite-type Bi 0.5 Sr 0.5 FeO 3 − δ (BSF55) and double perovskite PrBaCo 2 O 5+δ (PBCO) composite cathodes were prepared. The chemical compatibility of BSF55–PBCO composite material was confirmed by the absence of a secondary phase after firing below 850 °C for 2 h and annealing below 700 °C for 100 h. The electrode resistance of composite cathodes is indicated by Nyquist plots, all consisting of one arc in the high frequency (HF) range and another in the low frequency (LF) range. At 450 and 500 °C, the resistance in the HF range decreased linearly as the PBCO fraction increased, while BP73 showed the smallest arcs in the LF range. The activation energy of electrode resistance clearly decreased with the addition of up to 30 vol.% PBCO. This implies the mechanism of the oxygen reduction reaction underwent some changes due to the added PBCO. Considering the activation energy of the electrode resistance and the P(O 2 ) dependence of resistance at 700 °C, the addition of PBCO to BSF55 was shown to affect not only the mechanism but also the rate-determining step of oxygen reduction.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.