Abstract

Ferroelectric polymer/ceramic structure thin films were fabricated on Pt/SiO/sub 2//Si substrates using a sol-gel method. The bilayer thin film was composed of polar /spl beta/-phase poly(vinylidene fluoride) (PVDF) and 1 /spl mu/m thickness of polycrystalline lead titanate (PbTiO/sub 3/) thin film. By changing the concentrations of PVDF solutions (0.6/spl sim/1.0 M), various thickness of PVDF thin films (50-580 nm) were obtained, and the effects of various processing parameters on the characteristics of PVDF/PbTiO/sub 3/ thin films were studied. The characteristic of the /spl beta/ phase at infrared spectrum of 511 and 840 cm/sup -1/ can be observed in PVDF film crystallized at 65/spl deg/C for 2 h. With the increase of the PVDF thickness of the PVDF/PbTiO/sub 3/ films, the relative dielectric constant (/spl epsi//sub r/) decreased from 63 to 20 and the leakage current density (J) also decreased from 1.54 /spl times/ 10/sup -6/ to 3.86 /spl times/ 10/sup -7/ A/cm/sup 2/.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.