Abstract
Perovskite solid solution of Sr(Zr1-xAlx)O3-x/2 was prepared by a coprecipitation method using corresponding aqueous solutions and ammonium carbonate solution. The freeze-dried powders at x = 0-0.5, heated at 1000°C for 4 h in air, were identified to be an orthorhombic SrZrO3 solid solution. The highest electrical conductivity of Sr(Zr1-xAlx)O3-x/2 system sintered at 1400°C was measured at x = 0.2 (3.80×10-4 S/cm at 800°C, activation energy 109 kJ/mol ). The activation energy also showed a maximum value at x = 0.25 .
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.