Abstract
In the present paper, a new kind of duplex stainless steel (DSS, 00Cr22Ni6MnMoCu) was prepared. Cr30 was chosen as a comparison of microstructures and mechanical properties with 00Cr22Ni6MnMoCu. Corrosion tests with 3.5% NaCl solution and electrolytic solution for 00Cr22Ni6MnMoCu were carried out to analyze the corrosion pattern of test materials. It can be concluded that: (1) Austenitic and ferrite duplex stainless steel has an optimized phase distribution, high toughness and strength when the ratio of two-phase content is 1:1. (2) Corrosion tests show that the corrosion resistance of 00Cr22Ni6MnMoCu is 12 times compared to ferrite stainless steel Cr30. (3) Electrolytic corrosion tests show that for 00Cr22Ni6MnMoCu, the corrosion is caused by intergranular corrosion. For Cr30, it is mainly caused by pinholes. However, Cr30 has a poor corrosion resistance because of the presence of a large amount of carbides and their phase boundaries caused by the electric potential difference between the carbide and the matrix.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.