Abstract
The nitrate–citrate gel exhibits auto-catalytic behavior, which can be used to synthesize nanocrystalline YIG powders. In this study, yttrium iron garnet (Y 3Fe 5O 12) nanocrystalline powders were prepared by a sol–gel auto-combustion process. The influence of metal nitrates to citric acid molar ratio (MN/CA) of the precursor solution on the combustion behavior and crystallite size of synthesized powders was investigated by scanning electron microscopy (SEM), thermal analyses (DTA/TGA) and X-ray diffraction (XRD). The results show that with increasing MN/CA value, the combustion rate increases and the single-phase YIG forms at a higher temperature. The crystallite size of the single phase YIG prepared with different MN/CA values and calcined at 800 °C for 3 h are in the range of 38–70 nm. In addition, the crystallite size of the powders increased with increasing the calcination temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.