Abstract
The goal of this study was to investigate the feasibility of spray drying to produce microparticles of oxidized cellulose (OC), a biocompatible and bioresorbable polymer. OCs containing 7, 13, and 20 wt% carboxylic groups were converted into stable aqueous dispersions and then spray dried using a Yamoto G-32 spray dryer, equipped with a standard fluid nozzle with an orifice of 406 μm. The following operating conditions were investigated: inlet temperature 140, 170, and 190°C; feed rate 3, 6, and 9 mL / min; and atomization air pressure 0.5, 1, and 1.5 kg f/cm2. The amounts of OC used in feed were 1, 2.5, and 5%. OC microparticles produced under these conditions were shrunken spheres, ranging in size between 0.98 ± 0.47 and 2.05 ± 0.98 μm. The different operating conditions used had no significant effect on the size and shape of particles. The use of a water-soluble plasticizer (glycerin, polyethylene glycol 400, or polyethylene glycol 6000) in the dispersion yielded microparticles with a good sphericity and a smooth surface morphology, whereas no change in the shape or size of microparticles was noted with water-insoluble plasticizers, Triacetin® and dibutyl phthalate. Powder X-ray diffraction and Fourier transform infrared spectral analyses of spray-dried microparticles showed no change in the solid-state structure of OC. In conclusion, results show that OC can be converted into stable aqueous dispersions and used to produce microparticles by spray drying.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.