Preparation and characterization of semi-IPNs of polycaprolactone/poly (acrylic acid)/cellulosic nanowhisker as artificial articular cartilage

Abstract

Cartilage is a semi-solid resilient and smooth elastic connective tissue and upon damage, its repair is almost impossible or occurs with a very slow recovery process. Polycaprolactone (PCL), used as a biocompatible polymer, withholds all required mechanical properties, except suitable cell adhesion due to its hydrophobicity. In order to resolve this issue, we sought to introduce appropriate semi-IPNs into the system to regain its hydrophilicity base on increasing of the hydrophilic polymer. PCL and Cellulose nanowhiskers (CNWs) were entrapped in a network of poly (acrylic acid) that had been crosslinked via a novel acrylic-urethane crosslinker. The influential synthetic parameters on the preparation of artificial articular cartilages were investigated based on the Taguchi test design. The prepared CNW, acrylic-urethane crosslinker and semi-IPNs were studied via 1H NMR, FTIR, SEM, TEM, TGA, water swelling, water contact angle, tensile, and MTT analyses. According to the results, the optimal amount of monomer was about 46%. Incorporation of an optimized amount of CNW, which was 0.5%, improved the mechanical properties of artificial cartilage. After a 30 h time period, semi-IPNs showed the water absorption of about 30%. MTT on days 1, 3 and 5, as well as cell attachment, confirmed the biocompatibility of the semi-IPNs.