Preparation and Characterization of Semi‐IPN Fluorine Containing Polybenzimidazole/Nafion Composite Membrane for Fuel Cells

Abstract

AbstractA facile way to prepare semi‐interpenetrating polymer network (semi‐IPN) membrane which adopted 1,3‐benzenedisulfonyl azide (1,3‐BDSA) to crosslink with fluorine containing polybenzimidazole (Aliphatic‐16F‐PBI) in the Aliphatic‐16F‐PBI/Nafion composite membranes was proposed. By means of Fourier transformed infrared (FTIR) spectra analysis, the possible crosslinking reaction mechanism was investigated. Results suggested that 1,3‐BDSA molecule loses a nitrogen and forms nitrene upon heating. Then this nitrene reacts with C–H bond of Aliphatic‐16F‐PBI. Scanning electron microscope (SEM) images showed that the compatibility of PBI and Nafion improved while hexadecafluoro‐octyl groups were implanted into Aliphatic‐16F‐PBI molecule. The properties of Aliphatic‐16F‐PBI/Nafion composite membranes for fuel cell applications were determined through tests of gel fraction, thermogravimetry (TG), dimensional stability, mechanical property and proton conductivity. The gel fraction could reach 27.9% when 7.4% 1,3‐BDSA was added into the composite membranes. The proton conductivity of the semi‐IPN Aliphatic‐16F‐PBI/Nafion composite membranes could reach 0.69 × 10–2 S cm–1 at 120 °C at 100% relative humidity. Such high crosslink degree resulted in the improvement of the tensile strength, dimensional stability and chemical oxidative stability of semi‐IPN Aliphatic‐16F‐PBI/Nafion composite membranes. Nonetheless, it had little effect on the thermal stability.