Abstract
The semi-carbonization method is a kind of waste treatment to carbonize rice straw fiber at low semi-carbon temperature. The rice straw fiber is carbonized incompletely, which serves as building materials additive. The results reveal that the optimized carbonization condition is at 313 °C for 20-40 min with H3PO4 as activator. The structure of semi-carbonized straw fiber displays a large quantity of micropores, with which the wall thickness and the pore diameter are in the range of 1-4 μm, presenting the iodine sorption value of 1 320-1 470 mL/g and the methylene blue sorption value of 1 330-1 460 mg/g, respectively. Moreover, the acidic oxygen-containing groups impart the structure higher sorption of polar molecules. The semi-carbonized rice straw fiber with open and closed micro-mesopores demonstrates good hygroscopicity, implying the potential application as a functional additive in building materials.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.