Abstract
AbstractThe high molecular weight polyacrylate self‐emulsifying emulsion with 20% hydroxyl monomer and 50% solid content was prepared. Waterborne polyester was used to modify the acrylate resin. Besides acrylic acid (AA) and methacrylic acid (MAA), poly(ethylene glycol) methyl ether methacrylate (PEGMEMA) was also used as functional monomer to stabilize the polymerization process and improve the properties of the emulsion. The effects of the amount of waterborne polyester (WP), ammonium persulfate (APS), poly(ethylene glycol) methyl ether methacrylate (PEGMEMA), methacrylic acid (MAA)/acrylic acid (AA) monomer ratio, butyl acrylate (BA)/styrene (St) monomer ratio on the molecular weight, particle size, viscosity, storage stability, and cured film properties of the polyacrylate emulsion were investigated. The average molecular weight of the modified polyacrylate was up to about 2.5 × 104 g mol−1. The emulsion remained stable after 6 months at room temperature. Transmission electron microscope (TEM) images showed that the latex particles had core‐shell structure. The films cured with melamine formaldehyde (MF) resin showed excellent water resistance, adhesion, and hardness.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.