Abstract
AbstractThe two poly(silyl ester)s containing 2,2‐bis(p‐dimethylsiloxy‐phenyl)propane units in the polymer backbones have been prepared via polycondensation reaction of di‐tert‐butyl adipate and di‐tert‐butyl fumarate with 2,2‐bis(p‐chloro dimethylsiloxy‐phenyl)propane to give tert‐butyl chloride as the condensate. The polymerizations were performed under nitrogen at 110°C for 24 h without addition of solvents and catalysts to obtain the poly(silyl ester)s with weight average molecular weights typically ranging from 5000 to 10,000 g/mol. Characterization of the poly(silyl ester)s included 1H NMR and 13C NMR spectroscopies, infrared spectroscopy, ultraviolet spectroscopy, differential scanning calorimetry, thermogravimetric analysis (TGA), gel permeation chromatography, and Ubbelohde viscometer. The glass transition temperatures (Tg) of the obtained polymers were above zero because of the introducing 2,2‐bis(p‐dimethylsiloxy‐phenyl)propane units in the polymer backbones. The TGA/DTG results showed that the obtained poly(silyl ester)s were stable up to 180°C and the residual weight percent at 800°C were 18 and 9%, respectively. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 101: 1937–1942, 2006
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.