Abstract

Piezo-/ferroelectric crystals of a new Pb(Yb1/2Nb1/2)O3-Pb(Mg1/3Nb2/3)O3-PbTiO3 ternary solid solution system with the dimensions of 30 × 30 × 12 mm3 have been grown by the top-seeded solution growth method for the first time. The crystal structure is analyzed by means of X-ray diffraction at various temperature. The composition of the grown crystals is found to be near the ternary morphotropic phase boundary. The Curie temperature TC reaches 205 °C. The piezoelectric coefficient d33 and the longitudinal electromechanical coupling factor k33 are found to be 1800 pC/N and 90%, respectively. A remanent polarization Pr of 27.8 μC/cm2 is displayed with a coercive field Ec of about 7 kV/cm. These results show that the PYMNT crystals exhibit a higher TC and a larger coercive field than the binary PMN-PT piezocrystals, making this material a promising candidate for high-power electromechanical transducers that can operate in a wider temperature range.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.