Abstract
Alumina aerogels were prepared by a sol–gel method combined with the ethanol supercritical drying technique using aluminum tri-sec butoxide and nitric acid as the precursor and catalyzer respectively. This method affords high-surface-area alumina aerogel monoliths without the use of complexing agents. The structure and morphology of the aerogels were investigated by TEM, XRD, FTIR and BET techniques. The results confirmed that the as-prepared alumina aerogel possessed a network microstructure made up of pseudoboehmite fibers and a surface area of 690m2/g. It was transformed to γ-Al2O3 after heat treatment at 800°C without a significant loss in surface area. DMA analysis and hotdisk thermal analysis were performed to characterize the mechanical and thermal properties of the samples. The results indicated that the alumina aerogel was robust and exhibited excellent thermal insulating properties. The elastic modulus was up to 11.4MPa after drying, which is the one of the highest modulus of alumina aerogels ever reported. The thermal conductivities at 30°C and 400°C were 0.028W/mK and 0.065W/mK respectively.
Sign-in/Register to access full text options 
Free) 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call