Abstract
Synthesis of machinable quality magnesium aluminium silicate (MgO-Al2O3-SiO2) for fabrication of insulators/spacers usable in high voltage applications under high vacuum conditions has been carried out following two different routes i.e. (i) sintering route, and (ii) glass route. A three-stage heating schedule involving calcination, nucleation and crystallization, has been evolved for the preparation of magnesium aluminium silicate (MAS) glass ceramic with MgF2 as a nucleating agent. The effect of sintering temperature on the density of compacted material was studied. Microstructure and machinability of samples obtained from both routes were investigated. They were also characterized for microhardness. Initial studies on material obtained by glass route reveal that these samples are superior to those obtained from sintered route in respect of their high voltage breakdown strength and outgassing behaviour. Outgassing rate of 10−9 Torr l·s−1 cm−2 and breakdown strength of 160 kV/cm were obtained. Different types of spacers, lugs, nuts and bolts have been prepared by direct machining of the indigenously developed glass ceramic.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.