A fatal disadvantage of continuously reinforced thermoplastic composites is the high melt viscosity of the matrix which hampers impregnation. However, the melt viscosity of low molecular weight CBT resin can reach extremely low value, which simplifies impregnation and enables the use of thermoset production methods. The thermal analysis, rheological analysis and mechanical property on the polymerization and crystallization of CBT into poly (cyclic butylene terephthalate) (PCBT) at different ratios of catalyst were investigated in this paper. The continuous glass fiber (GF) reinforced PCBT composite with over 70% fiber volume content was prepared via in situ polymerization, and the mechanical property of the PCBT was studied. The best impregnation time was decreased and the degree of crystallinity was increased respectively with catalyst fraction increasing. The tensile/flexural strength and modulus of PCBT resin and GF/PCBT composites were enhanced when the catalyst fraction increased from 0.3% to 0.6%.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.