Abstract
LiFePO4·xLi3V2(PO4)3 (LFP·xLVP, x=0, 0.05, 0.1, 0.15, 0.2) composites were prepared by the two-step solid-state method. The structure, morphology and electrochemical properties were characterized by X-ray diffraction, scanning electron microscope, cyclic voltammetry, charge-discharge performance test and electrochemical impedance spectroscopy. It was indicated that composites were presented rough in surface of ball-like particles. Two phase of LFP and LVP combination improved electrochemical properties of LFP. The LFP·0.1LVP has the highest discharge capacity of 154mAh/g at 0.2C. Compared with LFP, the rate performance of the LFP·0.1LVP increased 13% and 8% at 1C and 10C after five cycles. It possessed excellent cycle life of 99.8% after 100 cycles at 1C especially. The all preparation process without any solvent addition was easy operation, energy saving and environmentally friendly.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.