Abstract
In this study, p–n heterojunctions with La 0.5Sr 0.5CoO 3 (LSCO) and Al-doped ZnO (AZO) thin films were fabricated by the radio frequency (r.f.) magnetron sputtering technique. The LSCO/AZO heterojunction was obtained by stacking the p-type LSCO thin film on the annealed n-type AZO thin film under different Ar: O 2 sputter gas ratio atmosphere. The thickness of LSCO and AZO thin films are about 400 nm and 500 nm, respectively. Good crystalline match between LSCO and AZO films was observed from the SEM and XRD analysis. The heterojunction diode clearly demonstrated rectifying behavior in the range of −8 to +8 V in reverse shape. The turn-on voltage of the diodes is obtained around 1.5 V and is in agreement with the value obtained from the difference in the work functions of LSCO and AZO. The band structure of the heterojunction was proposed based on the results of analysis.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.