Abstract
We report on the preparation of electroactive β-phase in polyvinylidene fluoride hexafluoropropylene (PVDF-HFP) without any electrical poling treatment. The PVDF-HFP film with various mass fractions (wt%) of magnesium chloride hexahydrate salt (MgCh∼6H2O) was fabricated by a solution casting technique. The morphological, mechanical, structural and dielectric properties were investigated. Results founded that the PVDF-HFP composite films show a large number of micro-pores on the top surface as a sponge-like structure. The Young’s modulus and crystallinity values tend to be linearly decreased with the MgCh2⋗6H2O concentration leading to enhance flexibility. The largest β-phase fraction of 87.2% is found in the composite with 1 wt% MgCh2⋗6H2O filler. The obtained value is 4 times higher than the value of unfilled PVDF-HFP. Moreover, the maximum value of dielectric constant is about 19.2 at 10 Hz for 4 wt% MgCh2⋗6H2O filler. Therefore, the modified composites with the excellent flexibility, dielectric constant and β-phase may be a promising material for applications in the field of piezoelectric energy conversion.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IOP Conference Series: Materials Science and Engineering
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.