Abstract
Ethylene vinyl acetate (EVA)/natural rubber (SMR L)/organoclay thermoplastic elastomer nanocomposites were melt compounded in an internal mixer, Haake Rheometer, at 120°C and 50 rpm rotor speed. In this paper, we demonstrate the effect of different blending sequences and organoclay loading from 2 to 10 phr (parts per hundred resins) on the tensile properties, morphology, thermal degradation, flammability, and water absorption behavior of EVA/SMR L/organoclay nanocomposites. EVA/SMR L/organoclay TPE nanocomposites were prepared by three different blending sequences, and each exhibited different tensile properties. Results indicated that the presence of organoclay increases the tensile properties, resistance toward thermal degradation, resistance to water permeation, and flame retardancy for all the nanocomposites prepared via different blending sequences. However, the optimum results for all the properties studied were achieved when EVA was blended with organoclay first and SMR L was incorporated later into the blend. The optimum organoclay loading was achieved at 2 phr. Results from scanning electron microscopy (SEM) and X-ray diffraction (XRD) studies showed that at 2 phr organoclay loading, nanostructures of individual silicate layers were achieved, whereas at 8 phr organoclay loading, agglomeration was observed. Flammability of the nanocomposites decreased when the organoclay loading increased.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.