Abstract
Carboxymethyl cellulose (CMC)-polyvinyl alcohol (PVA) and chitosan (CS)-polyvinyl alcohol were cross-linked by Fe3+and glutaraldehyde respectively to prepare cation exchange layer and anion exchange layer, and polyvinyl alcohol-sodium alginate (SA)-metal octocarboxyphthalocyanine (MePc (COOH)8, a kind of water splitting catalyst, here, Me stands for Fe3+or Co2+) nanofibers were prepared by electrospinning technique and introduced into the interlayer to obtain the CMC-PVA/PVA-SA-MePc (COOH)8/CS-PVA bipolar membrane (BPM). The experimental results showed that compared with the BPM without the PVA-SA-MePc (COOH)8interlayer, the water splitting efficiency at the interlayer of the CMC-PVA/PVA-SA-MePc (COOH)8/ CS-PVA BPM was obviously increased, and its membrane impedance decreased. When the concentration of FePc (COOH)8in the PVA-SA-FePc (COOH)8nanofibers was 3.0%, the trans-membrane voltage drop (IRdrop) of the CMC-PVA/PVA-SA-FePc (COOH)8/CS-PVA BPM was as low as 0.6V at a high current density of 90 mA/cm2.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.