Abstract
In this study, with La0.8Sr0.2Cr0.5Fe0.5O3-δ (LSCrF) and Ce0.8Sm0.2O1.9 (SDC) taken as the electronic conducting phase and the oxide ion conductor, respectively, dual-phase composite ceramic membranes with or without 3 % (in mole) Y2O3 stable ZrO2 (3YSZ) support were prepared and tested as oxygen separation membranes. Then, the oxygen transmission performance was tested by the electrochemical method based on the limiting current. The results obtained with this method coincide with those acquired by means of gas chromatography. Furthermore, the dependences of oxygen permeation rate on oxygen partial pressure, temperature and ceramic membrane thickness were analyzed. When air was used as the sweeping gas on the porous 3YSZ supported SDC-LSCrF dual-phase membrane, the oxygen permeation rate can reach 0.73, 0.82, 0.90 and 0.97 mL cm−2 min−1 at 650, 700, 750 and 800 °C, respectively.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.