Abstract
AbstractCrosslinked polybenzimidazole (PBI) was synthesised via free radical polymerisation between N‐vinylimidazole and vinylbenzyl substituted PBI. The degree of crosslinking increases with increasing content of the crosslinker. The phosphoric acid doping behaviour, mechanical properties, proton conductivity and acid migration stability of crosslinked PBI and linear PBI are discussed. The results show that the acid doping ability decreases with increasing degree of crosslinking of PBI. The introduction of N‐vinylimidazole in PBI is beneficial to its oxidation stability. The mechanical stability of crosslinked PBI/H3PO4 membrane is better than that of linear PBI/H3PO4 membrane. The proton conductivity of the acid doped membranes can reach ∼10–4 S cm–1 for crosslinked PBI/H3PO4 composite membranes at 150 °C. The temperature dependence of proton conductivity of the acid doped membranes can be modelled by an Arrhenius relation. The proton conductivity of crosslinked PBI/H3PO4 composite membranes is a little lower than that of linear PBI/H3PO4 membranes with the same acid content. However, the migration stability of H3PO4 in crosslinked PBI/H3PO4 membranes is improved compared with that of linear PBI/H3PO4 membranes.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.