Abstract
Multiwalled carbon nanotube (CNT) reinforced aluminum nanocomposite coatings were prepared using cold gas kinetic spraying. Spray drying was used to obtain a good dispersion of the nanotubes in micron-sized gas atomized Al–Si eutectic powders. Spray dried powders containing 5 wt.% CNT were blended with pure aluminum powder to give overall nominal CNT compositions of 0.5 wt.% and 1 wt.% respectively. Cold spraying resulted in coatings of the order of 500 μm in thickness. Fracture surfaces of deposits show that the nanotubes were uniformly distributed in the matrix. Nanotubes were shorter in length as they fractured due to impact and shearing between Al–Si particles and the Al matrix during the deposition process. Nanoindentation shows a distribution in the elastic modulus values from 40–229 GPa which is attributed to microstructural heterogeneity of the coatings that comprise the following: pure Al, Al–Si eutectic, porosity and CNTs.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.