Abstract
We present a high entropy alloy (HEA) from the system Al-Co-Cr-Fe-Ni with small additions of W, Mo, Si and C which was designed to allow for precipitation hardening by annealing in the temperature range from 600 to 900 °C. The alloy development was supported by thermodynamic computations using ThermoCalc software and the specimens were produced by arc melting. The microstructure of one selected sample in as-cast and annealed conditions was analysed using SEM/EDS, SEM/EBSD and TEM. The as-cast microstructure consists of spinodally decomposed BCC dendrites enveloped by FCC+Cr23C6 eutectic. Upon annealing at 700 °C for 24 h nanoscale precipitates form within the spinodal BCC as well as from FCC. Precipitation is exquisitely uniform leading to an increase in microhardness from 415 HV0.5 in the as-cast state to 560 HV0.5 after annealing. We investigated coarsening of this microstructure using varying holding time for a constant temperature of 700 °C. The microstructure evolution during coarsening and the corresponding mechanical properties obtained from instrumented indentation experiments are presented in this work.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.