Precipitation behavior of carbides and cryogenic toughness in heat-affected zone of high-Mn twinning-induced plasticity steel welded joint

Abstract

The newly designed cryogenic high-Mn steel plates (Fe-23Mn-1.5Al-0.45C) were joined by metal inert gas (MIG) multi-pass welding process. To evaluate the inhomogeneity of microstructure and cryogenic toughness in heat-affected zone (HAZ) of welded joint, the impact samples were prepared by zonal sampling method. The microstructure features and embrittlement mechanism in HAZ of welded joint were systematically investigated. The results reveal that grains obviously grew in the coarse-grain HAZ (CGHAZ). C element segregated and nano-sized lamellar and granular (Cr, Mn) 7 C 3 carbides precipitated at the grain boundary in HAZ, and the size of precipitate carbides in CGHAZ and fine-grain HAZ (FGHAZ) was about 100 nm and 40 nm, respectively. The interface between (Cr, Mn) 7 C 3 and γ-austenite matrix in CGHAZ was incoherent with the lattice misfit of 45.13%. Higher fraction of low angle grain boundaries (LAGBs) appeared in CGHAZ (25.89%) and FGHAZ (11.99%), compared with the base metal (4.33%). Such microstructural differences can degrade the impact toughness in CGHAZ. From cryogenic Charpy impact tests, the impact toughness in different zones of the joint at each test temperature follows this sequence: base metal > fine-grain HAZ > coarse-grain HAZ > fusion line. These results can provide a fundamental understanding and guidance on the brittle failure of cryogenic high-Mn steel welded joint during service.