The effect of carbidization on the morphology of iron oxyhydroxide particles has been studied. Homogeneous oxidation of iron(II) sulfate results in predominantly γ-FeOOH particles which have a rod-shaped crystalline structure. Carbidization of the prepared iron oxyhydroxide particles at 270 °C and atmospheric pressure without mechanical stirring was found to produce iron carbides with spherical layered structure residing in close proximity. HRTEM, EDS and electron microdiffraction analysis revealed that carbidization alters the initial nanoneedle-type morphology and generates ultrafine carbide particles with irregular spherical shape. When carbidization was performed under severe mechanical stirring, formation of spherical carbide particles completely separated from each other was obsrved. Initial activity of iron oxyhydroxide for Fischer-Tropsch synthesis was found to be high (a CO conversion of about 84%) which declined steadily with synthesis time (26% CO conversion after 340 h of synthesis). The effect of carbidation on the morphology of iron hydroxide oxide (γ-FeOOH) particles with a three dimensional crystalline nanoneedle structure has studied. Carbidation of γ-FeOOH with CO at atmospheric pressure produced iron carbides with spherical layered structure. HRTEM and EDS analysis revealed that carbidation changes the initial nanoneedles morphology and generates ultrafine carbide particles with irregular spherical shape.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.