Abstract
The effect of cold deformation and aging on the microstructure and properties of Cu-3Ti-2Mg alloy was investigated. The microstructure and phase constituents were characterized by optical microscope (OM), scanning electron microscope (SEM), X-ray diffractometer (XRD), transmission electron microscope (TEM) and electron backscattering diffraction (EBSD), and the hardness and electrical conductivity were measured as well. The results show that the microstructure of as-cast Cu-3Ti-2Mg alloy consists of Cu2Mg phase, plate-like Cu4Ti phase and Cu matrix. The microstructural characterizations reveal that the βprime;-Cu4Ti phase precipitates from the supersaturated Cu matrix during aging. However, excessive aging causes the phase transformation from metastable, coherent βprime;-Cu4Ti to equilibrium, incoherent Cu3Ti phases. In the range of experiments, the optimum process for Cu-3Ti-2Mg alloy is solutizing at 700 °C for 4 h, cold deformation of 60%, and aging at 450 °C for 2 h. The electrical conductivity and hardness HV of Cu-3Ti-2Mg alloy are 16.7 %IACS and 3280 MPa, respectively.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call