Abstract

In this work, polyethyleneglycole (PEG) is introduced into polypyrrole (PPy) film coated on LiFePO 4 powder particles to promote the properties of cathode material for lithium-ion batteries. The enhancement of the electrochemical activity by the substitution of a carbon with electrochemically active polymer is investigated. Films of the PPy doped with the PEG were prepared by the chemical oxidative polymerization of pyrrole (Py) monomer. PEG has been added as an additive during polymerization process to improve mechanical and structural properties of the PPy in final PPy/PEG–LiFePO 4 cathode material. Cyclic voltammetry (CV), electrochemical impedance spectroscopy (EIS) and galvanostatic charge/discharge measurements were employed to characterize the electrochemical properties of PPy/PEG–LiFePO 4 material. The electrochemical performance of PPy–LiFePO 4 electrodes was greatly improved by introduction of PEG into the PPy films. Charge/discharge measurements confirmed the increase in capacity when applying PEG in PPy. The morphology and particle sizes of the prepared cathode powder material were investigated by scanning electron microscopy (SEM) and particle size analysis (PSA). Distribution of PPy and PPy/PEG films onto the LiFePO 4 particles surface was studied by time of flight secondary ion mass spectrometry (TOF-SIMS). In addition to polymeric coating layer on the surface of PPy–LiFePO 4 composite particles, some PPy unequally distributed between the particles was found. The median diameter value is 4.92 μm for PPy–LiFePO 4 sample. TOF-SIMS measurements and SEM images confirmed that thickness of polypyrrole coating on LiFePO 4 particles is about 100 nm.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.