Abstract
Powder quartz (PQ)/nano-TiO2 composite was prepared by a mechanochemical method. Based on as-prepared PQ/nano-TiO2 composite, we prepared interior paints and investigated the degradation efficiency of formaldehyde (DEF). Scanning electron microscopy showed that nano-TiO2 got well dispersed by the adding of PQ. Thermogravimetric analysis indicated that the mass ratio of 4:1 was a relatively good proportion for the most production of PQ/nano-TiO2 composite. Fourier transform-infrared spectrometry showed that the peak position of Ti-O-Si bond varied with the milling time. At the early stage, no characteristic peak of Ti-O-Si bond was observed, while at the later stage, new peaks at 902 cm-1 and 937 cm-1 appeared. Meanwhile, PQ/nano-TiO2 composite-based interior paint exhibited significant DEF of 96.3% compared to that consisting of sole nano- TiO2 of 92.0% under visible light illumination. As an abundant mineral resource, PQ would make interior paints with HCHO purifying effect much more efficient and cheaper.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Wuhan University of Technology-Mater. Sci. Ed.
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.