Abstract
The crystallographic and microstructural parameters of plasma sprayed pure zirconia powders were studied by X-ray and neutron powder diffraction. A significant influence of the flow rate of the quenching gas on the phase composition (the tetragonal to monoclinic ratio varied between 0.6 and 3.5) and on the micro-structure was observed, while structural parameters of both phases of all investigated samples remained essentially unchanged and were close to those reported in the literature. These results do not support the concept of a critical particle size effect as a stabilizing factor for the tetragonal phase. A transition from a tetragonal to a monoclinic phase was observed without any measurable change in the crystallite sizes by heating at 845‡C. A very high background on the neutron powder patterns may have been caused by the presence of pores in the samples.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.