Abstract
Atom Probe Tomography has been performed on as-irradiated and post-irradiation annealed surveillance weld samples from Ringhals Unit 3. The weld contains low Cu (0.07at.%) and high Ni (1.5at.%). A high number density (∼4×1023m−3) of Ni–Mn–Si-enriched clusters was observed in the as-irradiated material. The onset of recovery was observed during the annealing for 30min at 450°C. Much more significant dissolution of clusters occurred during the 10min 500°C anneal, resulting in a reduction in mean cluster size and a halving of their volume fraction.Detailed analyses of the changes in microstructure demonstrate that the dissolution process is driven by migration of Mn atoms from the clusters. This may indicate a strong correlation between Mn and point defects. Dissolution of the clusters is shown to correlate with recovery of mechanical properties in this material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.