ABSTRACTTo study the nature of irradiation-induced nanofeatures in oxide dispersion strengthened (ODS) Fe-Cr alloys, post-irradiation isochronal thermal annealing up to 600°C was performed for ODS Fe-9%Cr and Fe-14%Cr alloys ion-irradiated at 300°C and 500°C. Nanoindentation indicated hardening for all as-irradiated alloys and complete hardness recovery upon post-irradiation annealing. Cross-sectional TEM indicated an irradiation-induced defect band near peak damage mainly consisting of dislocation loops. Candidate mechanisms of recovery were critically evaluated. Shrinkage of loops via capture of thermal vacancies was found to correctly reflect the annealing behaviour of ODS Fe-9Cr irradiated at 300°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.