Abstract
AbstractPoly epoxy is a high performance room temperature cured epoxy system which provides excellent physical and mechanical properties. However, the effects of post curing of this resin system on the properties of different sandwich structures are unknown. This study aims to evaluate the effect of post curing (at 70°C for 2 hr) on the edgewise compressive and flexural strengths of a sandwich structure, constructed with Styrofoam and honeycomb as core materials and a plain weave carbon fabric as face sheet. Tested factors evaluated from edgewise compressive tests were as follows: peak load, compressive strength, and crash energy absorption of sandwich structures while core shear stress and bending stress of sandwich structures were determined and compared with flexural tests. It was observed that post curing affects significantly on the bending and compressive strengths of the sandwich structures. However, the data obtained for crash energy absorption suggested that the effect of post curing on the core shear strength and the total deflection was statistically insignificant. The matrix polymer was also inspected using dynamic‐mechanical thermal analysis to assess the changes in glass transition temperature and degree of conversion due to post cure. POLYM. COMPOS., 2013. © 2013 Society of Plastics Engineers
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.