Abstract
We report here structural and I–V characteristics of ZnO varistor with Fe2O3 nanoparticles additions (≤200 nm). It was found that the addition of Fe does not influence the wurtzite structure of ZnO ceramics, while the average grain size was affected. Interestingly, the nonlinear region was clearly observed in the I–V characteristics of the samples with Fe = 2.5%, 5% and 10%. Whereas, two nonlinear regions were only observed with further increase of Fe addition above 10% (30% and 50%). Although the values of non-linear coefficient are decreased by the additions of Fe, the breakdown field could be increased up to 7900 V/cm. Furthermore, the electrical conductivity was improved by increasing Fe up to 10%, followed by a decrease with further increase of Fe up to 50%. These results were discussed in terms of Fe2O3 nanosize grains which were formed and localized at the grain boundaries of ZnO ceramics.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.