Abstract
AbstractPositron annihilation lifetime spectroscopy and differential scanning calorimetry (DSC) measurements were performed for blends of polyacrylamide (PAM) and poly(ethylene glycol) (PEG) and blends of poly(dimethylacrylamide) (PDMAM) and PEG. The samples were prepared by codissolution in a concentration range of 0–100 wt % PEG. The thermal behavior, characterized by DSC measurements, showed similar variations of the glass‐transition temperatures (Tg's) with the PEG concentration for the two systems. Pure PAM and PDMAM presented Tg's of 188 and 111 °C, respectively. A relatively small and nearly linearly decreasing Tg was observed for the two systems in the range of 20–80 wt % PEG. PEG crystals were present in all blend compositions, and no melting point depression was observed. The thermal results pointed to the partial miscibility of the blends. The degree of crystallinity of PEG increased with increasing PEG concentration for the PDMAM/PEG systems. The ortho‐positronium lifetime (τ3) increased with increasing PEG concentration for both blends. However, the parameter of the ortho‐positronium formation probability (I3) decreased with the PEG concentration. The product τI3, which was proportional to the total free volume fraction, was approximately constant with the PEG concentration for PDMAM blends and increased with the PEG concentration for PAM systems. This result may be interpreted as a consequence of a more heterogeneous structure in PAM blends. Scanning electron microscopy micrographs of blends with 40 and 80 wt % PEG provided evidence of the regions associated with PEG crystallites. © 2003 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 41: 1493–1500, 2003
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Polymer Science Part B: Polymer Physics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.