Abstract
The Portevin–Le Chatelier (PLC) effect in the Nimonic 263 superalloy was investigated by tensile test at a wide temperature ranges from 293 to 1033 K and strain rates between 0.1 and 6.25 × 10−6 s−1. Simple binary alloys Ni-0.4C, Ni-24Cr and Ni-5(8)Mo were also tested in order to identify which elements were responsible for the PLC effect in the Nimonic 263 alloy. The results demonstrated that for Nimonic 263 alloy, PLC effect occurred at certain temperatures and low strain rates. Normal PLC effect exhibiting type-A and -(A + B) serrations was attributed to the enhanced solute diffusion with increasing temperature, while inverse PLC effect with type-C serration was caused by unlocking process. The activation energy for the normal PLC effect was calculated to be 68 kJ/mol, and diffusion of substitutional solutes such as Cr and Mo was identified to be responsible for the PLC effect. In comparison with the PLC effect in simple binary alloys, solute atmospheres formed by different kinds of atoms in Nimonic 263 alloy work more effectively, increasing locking strength and corresponding mean stress drop magnitude.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.