Abstract
A facile and cost-efficient approach to functionalize raw carbon fiber paper (CFP) used for a self-standing capacitive electrode has been proposed here. Benefiting from the improved specific surface area and surface functional groups, the functionalized CFP (F-CFP) showed much enhanced capacitive performance, 3 orders of magnitude higher than that of the raw CFP. It delivered the areal capacitance of 1275 mF cm-2 at 5 mA cm-2 with a rather wide voltage window of 1.4 V (-0.4 to 1 V vs Ag/AgCl) in 0.5 M H2SO4. However, in a neutral 1 M Na2SO4 aqueous solution, although the areal capacitance of 1115 mF cm-2 at 3 mA cm-2 is slightly smaller, the potential window is much wider (2 V, -1 to 1 V vs Ag/AgCl), indicating a high overpotential of hydrogen evolution. The areal capacitance was still as high as 722 mF cm-2 at a very fast charge-discharge current density of 50 mA cm-2, and about 66% of the initial capacitance (at 3 mA cm-2) was remained in Na2SO4, indicating considerable rate capability.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.