Poplar wood treated with nano-silver–copper particles: fungal degradation and leaching analysis

Abstract

Abstract This study investigated the inhibition effect of nanoscale silver–copper particle (20 nm) against Coriolus versicolor and Gloeophyllum trabeum. Poplar wood samples (Populus L.) were vacuum-impregnated using aqueous nano-AgCu solutions at concentrations of 0.01 %, 0.02 %, 0.03 %, 0.05 %, 0.075 %, and 0.1 %. Alkaline copper quaternary (ACQ, 0.1 %), boric acid (0.2 %) and untreated control group (CK) were employed for comparisons. Decay resistance and leachability were studied. The anti-fungi effects were compared between nano-AgCu, nano-Ag, Ag+ (silver nitrate), Cu2+ (copper nitrate), and a composite of Ag+–Cu2+. Nano-AgCu particle exhibited effective resistance to fungi after 12 weeks of exposure. The threshold retention of the nano-AgCu against C. versicolor and G. trabeum on poplar wood was 0.19 kg m−3 and 0.62 kg m−3, respectively. The silver–copper nanoparticles demonstrated excellent leach resistance, and the inhibition effect was retained after leaching. The nano-AgCu particle provided better antifungal effects than single ions or metal nanoparticles. This study illustrates the potential of using nano-AgCu particle as an efficient wood preservative compared to commercial water-soluble preservatives.