Abstract
It is generally thought that, when a material is in its brittle to ductile transition, it is more difficult to design for crack arrest than to prevent crack initiation (cleavage). This report shows that this is not always true for weldments. Comparison is made between compact crack arrest (CCA), Ka, and crack tip opening displacement (CTOD), KJc, toughness for the same HY80 weld. The value of Ka is shown to be much higher than the minimum KJc for pop-in fracture initiation. It is considered that the results support the conclusion of Japanese research workers (Arimochi and Isaka) that small pop-ins (in the CTOD test) propagate and arrest without load drop. It follows that prediction of structural failure for weldments need not be based on minimum pop-in toughness from CTOD tests.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials and Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.