Abstract
Four polyurethane/polyamide copolymer dispersions (PUCON-co-APAS) were prepared from castor oil-based polyol (CON). Castor oil (CO) was firstly transesterified with triethanolamine at 210 °C for different time intervals: 30, 60, 90 and 120 min, to produce CON30, CON60, CON90 and CON120 polyols, respectively. The hydroxyl and acid values, density, viscosity, chemical structure analysis of the CON polyols were determined. The polyols were used to prepare PUCON30-co-APAS, PUCON60-co-APAS, PUCON90-co-APAS, and PUCON120-co-APAS copolymer dispersions in five steps using prepolymer self-emulsification solvent process. The first step is the prepolymer preparation step, in which CON was reacted with dimethylolpropionic acid and excess toluene diisocyanate to produce PUCON NCO . The second step is the copolymerization step, in which PUCON NCO was reacted with amino-terminated aromatic polyamide sulfone. The following processes are neutralization, chain extension and dispersion steps. The prepared copolymer dispersions were characterized using FTIR, DLS, TGA, DSC and GPC. Additionally, the physical, chemical and mechanical properties of the prepared copolymers were studied. The results showed an increase in the hydroxyl number of CON with increasing transesterification time. Stronger H-bonds and smaller particle sizes are produced using CON with higher transesterification time in the preparation of the copolymer dispersions.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.