Polyurethane—polystyrene interpenetrating polymer networks

Abstract

AbstractTwo component interpenetrating polymer networks (IPN) of the SIN type (simultaneous interpenetrating networks), composed of a polystyrene network (crosslinked with divinyl benzene) and a polyester‐polyurethane network (crosslinked with trimethylolpropane), were made. Electron microscopy and glass‐transition measurements showed that phase separation had resulted with some interpenetration, presumably occurring at the boundaries. At a composition of about 75 percent polyurethane, a phase inversion occurred, the continuous phase being polystyrene at polyurethane compositions of less than 75 percent. The stress‐strain properties and hardness measurements agreed with these results. Enhanced tensile strength was observed in the IPN's in a concentration range where modulus reinforcement was not evident. A small enhancement in tear strength and thermal stability was also noted.