Abstract
AbstractThe fracture behavior and deformation mechanisms of polypropylene modified by elastomeric metallocene‐catalyzed polyolefin blends were investigated under both static and dynamic loading conditions. The fracture toughness was evaluated with the J integral approach. The development of damage mechanisms was studied by the examination of fracture surfaces with scanning electron microscopy and by the examination of single‐edge, double‐notch, four‐point‐bending or low‐impact‐energy fractured samples with optical microscopy. In addition, tensile dilatometry measurements were carried out to determine the nature of the deformation micromechanisms. The fracture behavior and the size and shape of the damage zones were drastically influenced by the elastomeric particles and the imposed constraint. The role of the elastomeric particles was different, depending on the strain rate. Under impact loading, particle pullout and crazing were responsible for the increased fracture toughness of polypropylene. Under quasistatic loading, stable fracture growth was caused by particle cavitation, which promoted ductile tearing of polypropylene before failure continued in an unstable fashion via crazing. © 2004 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 42: 1075–1089, 2004
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Polymer Science Part B: Polymer Physics
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.