Abstract
The present study assessed the polymerization shrinkage stress kinetics of five low-shrinkage light-cured bulk-fill resin composites: Surefil SDR flow (SF, Dentsply), Tetric EvoCeram Bulkfil (TE, Ivoclar Vivadent), Venus Bulk Fill (VB, Heraeus Kulzer), x-tra fil (XF, Voco), and experimental bulk fill (FB, 3M ESPE). Filtek Z250 (FZ, 3M ESPE) was used as a control. Real-time shrinkage stress of investigated composites was measured using a tensometer; maximum shrinkage stress, stress rate (Rmax), and time to reach maximum stress rate (tmax) were recorded. Flexural strength and modulus were measured using a standard procedure, and curing efficiency of 4-mm long specimens was determined using bottom/top percentage Knoop microhardness. Data were analyzed using one-way analysis of variance and Bonferroni multiple range tests at a significance level of α=0.05. Results of shrinkage stress, Rmax, and tmax of all bulk-fill materials were significantly lower (p<0.05) than those of the control except for XF. All tested bulk-fill materials were able to achieve acceptable curing efficiency (≥80% bottom/top percentage) at 4-mm depth. In conclusion, this study reports a significant reduction in polymerization shrinkage stress while maintaining comparable curing efficiency at 4 mm for some bulk-fill composites and supports their potential use in posterior clinical situations.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.