Abstract
Volumetric shrinkage (VS) of conventional, bulk-fill, and core build-up resin-based composites (RBCs) of various thickness (1-5 mm) was measured using the modified bonded-disk method with confocal laser scanning microscopy. Additionally, the bottom-to-top ratio of Vickers hardness (%VH) was measured. Conventional RBCs exhibited significantly higher VS than bulk-fill and core build-up RBCs (p<0.05). As specimen thickness increased, VS relative to volume (%VS) and difference in VS at each depth (VSdepth) decreased. For conventional RBCs, there was a significant drop in VSdepth between 1 mm and 2 mm (p<0.05), and another drop was observed between 3 mm and 4 mm (p<0.05) where %VH decreased below 90%. For bulk-fill and core build-up RBCs, VSdepth decreased significantly between 2 mm and 3 mm (p<0.05), but %VH exceeded 90% even in 5 mm deep cavities. These results indicated that post-curing contributed to lower shrinkage in deeper layers, and that conventional RBCs were not adequately polymerized at the depth of over 3 mm.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.