Abstract
AbstractSolution‐processed inorganic perovskites cause chemical and structural defects unfavorable for photodetector application. Using a binary solvent, defects in CsPbIxBry (CPIB) perovskite are passivated with poly 4‐vinylpyridine (PVP) and Poly methyl methacrylate (PMMA) polymers. X‐ray photoelectron spectroscopy and FTIR spectra reveal a Lewis base‐acid interaction between Pb2+ and polymer, confirming the passivation of CPIB perovskite. Scanning electron microscopy analysis shows a dual‐surface morphology with microribbons and microcrystals in perovskites. After PMMA treatment, CPIB perovskite exhibits a blue shift in the bandgap (1.8 to 1.95 eV), while the PVP induced a redshift, reducing the bandgap to 1.7 eV. Blue shift in PL analysis indicates modification of grain boundaries. A higher lifetime obtained for CPIB/PVP confirms the restraint of non‐radiative recombinations. Photodetectors are fabricated with pristine CPIB, CPIB/PVP, and CPIB/PMMA perovskites. The passivated CPIB/PVP‐based photodetector exhibits a quick rise time of ≈23 ms and a decay time of ≈17 ms. It also demonstrates a remarkable photoresponsivity of 23 mA W−1, an internal quantum efficiency of 4.9%, and a detectivity of 15.0 × 1010 Jones at 10 mW cm−2 light intensity. This approach shows the potential for environmentally stable polymers to passivate inorganic perovskites for high photodetection performance.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.