Abstract
Polymer film capacitors are usually limited to relatively low working temperatures due to the large conduction loss of polymer dielectrics under high thermal stress. Here, a polymer dielectric sandwiched by medium-dielectric-constant nanoscale deposition layers is reported, which exhibits significantly suppressed conduction loss and outstanding capacitive performance at high temperatures. A series of deposition materials with distinct band structures and dielectric properties are investigated. It is found that well-balanced bandgap, dielectric constant and electrical conductivity of the nanoscale deposition layer is desirable for suppressing charge injection. The substantial performance improvements are demonstrated to result from the slow decay of barrier height with increasing electric field and the reduced electric field in the deposition layers. The optimized design using a polyetherimide film sandwiched by 150-nm-thick Al2O3 deposition layers gives rise to a concurrent high discharged energy density (2.8 J cm−3) and charge-discharge efficiency (90%) up to 200 °C, which are significantly higher than those of previously reported surface-coated polymer dielectrics, and are even comparable to the maximum values achieved with expensive, less productive solution-based composite approaches. Moreover, the nanoscale coating layer can be fabricated through evaporation deposition techniques, which is accessible with industrial equipment for fast surface deposition of capacitor films
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.