Abstract
In this study, simvastatin (SIM) drug incorporated poly(d,l-lactic-co-glycolide) (PLGA)/biphasic calcium phosphate (BCP) composite material (SPB) was coated on the BCP/ZrO2 (SPB-BCP/ZrO2) scaffold to enhance the mechanical and bioactive properties of the BCP/ZrO2 scaffold for bone engineering applications. The composite coating was prepared by combining different ratios of PLGA and BCP (1:2, 1:1, 2:1). After completion of the coating process, the compressive strength of the scaffolds was shown to increase with an increase in PLGA concentration from 8.5 ± 0.52 MPa for the SPB1-BCP/ZrO2 (1:2) to 11 ± 0.65 MPa for SPB3-BCP/ZrO2 (2:1) scaffolds when PLGA concentration was increased. Furthermore, the increase of PLGA in the coating composition corresponds to a decrease in porosity, degradation rate and weight loss of the scaffolds after 4 weeks. SIM release study demonstrated sustained release of the drug for the three kinds of scaffolds with improved biocompatibility. The increase of PLGA concentration also resulted in a lower release rate of SIM. Thus, the lower release rate of SIM brought upon by the increase of PLGA concentration further enhanced the performance of the scaffold in vitro making it a promising approach in the field of bone tissue regeneration.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.