Abstract
ABSTRACT In this study, unidirectional flax fabrics were used to reinforce poly(lactic acid) (PLA). Flax/PLA composites were produced by thermo-compression using as-received flax fibers and titanium dioxide (TiO2) coated flax fibers. The aim was to investigate the effect of annealing temperature and time, under quiescent or mechanical stress conditions, on the microstructure, interfacial adhesion, crystallization, and mechanical properties of composites. Results showed significant differences between oxidized-TiO2-coated flax fibers/PLA composites (oxi-TiO2-C) and as-received flax fibers/PLA composites (AR-C). Indeed, above the glass transition temperature (Tg) of PLA, the storage modulus (E’) of both composites significantly increased due to PLA crystallization. However, once E’ reached a maximum value, composites with treated flax fibers leveled off while the E’ of composites with untreated flax fibers dropped drastically. This peculiar result was explained by a partial destruction or damage of AR-C interface during PLA crystal growth. This phenomenon was not observed with oxi-TiO2-C, suggesting a good interfacial adhesion. Despite the presence of a trans-crystalline layer for both samples, it was shown that TiO2 coating of flax fibers strengthened the adhesion between flax fibers and the trans-crystalline structure. Interlaminar shear strength measurements revealed a 15% increase in the interfacial strength.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.