Abstract
Polyethylene oxide (PEO)-polypropylene oxide (PPO)-polyethylene oxide block copolymer having different molecular weights are used as precursors of carbon materials to prepare Hollow -Derivatives carbon material as an electrocatalyst through block copolymer self-assembly. The composition and microstructure of the prepared catalysts are shown by Raman spectroscopy, X-ray diffraction (XRD), Test of nitrogen adsorption and desorption curves, High resolution transmission electron microscopy (HR-TEM) and scanning electron microscopy (HR-SEM). Oxygen was passed into alkaline electrolyte solution until the solution reached saturation state. With molecular weight increasing, the obtained sample gradually changed from block to hollow and spherical. When the molecular weight was 12600 g mol−1, the evenly hollow carbon nanocages was acquired (C-12600). In O2 saturated alkaline electrolyte (0.1 M KOH solution), C-12600's limited current density,half-wave potential and initial potential are 5.23 mA cm−2@0.4 V, 0.72 V and 0.81 V, respectively. And most important is that half-wave potential and onset potential have barely change after 2000 cycles of cyclic voltammetry. As a result, the porous carbon materials exhibited excellent electrocatalytic activity while maintaining high stability in alkaline KOH solution.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.